Abstract

Durability rather than high strength appears to be the principal characteristic for high-performance concrete mixtures being developed for use in hostile environments such as seafloor tunnels, offshore and coastal marine structures, and confinement for solid and liquid wastes containing hazardous materials. Strength, dimensional stability, impermeability, and high workability are usually the principal characteristics required of high-performance concrete.

In this paper an overview of the composition of concrete and its effect on the properties desired for high performance is given. This overview can be used as a basis for selection of component materials and mix proportioning. A new step-by-step procedure for mix proportioning is described. The calculated mix proportions from this procedure appear to be consistent with the state-of-the-art laboratory and field practice. Also, a brief review is given of concrete production and construction practices essential for making a high-performance end product.

Issue Section:
Research Papers
Keywords:
concrete strength, impermeability, durability, high performance, dimensional stability, cement paste, aggregate, mineral admixtures, superplasticizer, proportioning, strength grading

References

1.
Birchall
,
J. D.
, and
Kelly
,
A.
, “
New Inorganic Materials
,”
Scientific American
 0036-8733, Vol.
248
,
1983
, p. 104.
2.
Roy
,
D. M.
 and
Gouda
,
G. R.
, “
Optimization of Strength in Cement Pastes
,”
Cement and Concrete Research
 0008-8846, Vol.
5
, No.
2
,
1975
, pp.
153
-
162
.
Google Scholar
Crossref
Search ADS
 
3.
Mehta
,
P. K.
,
Concrete: Structure, Properties, and Materials
,
Prentice-Hall, Inc.
,
New York
,
1986
.
4.
Mehta
,
P. K.
, and
Aïtcin
,
P. C.
, “
Microstructural Basis for Selection of Materials and Mix Proportions for High Strength Concrete
,”
Proceedings
,
Berkeley Conference on High Strength Concrete
,
05
1990
.
5.
Aïtcin
,
P. C.
, and
Mehta
,
P. K.
, “
Effect of Coarse Aggregate Type on Mechanical Properties of High-Strength Concrete
,”
ACI Materials Journal
 0889-325X, Vol.
87
, No.
2
, March–April 1990, pp.
103
-
107
.
6.
Hanna
,
E.
,
Luke
,
K.
,
Perraton
,
D.
, and
Aïtcin
,
P. C.
, “
Rheological Behavior of Portland Cement Pastes in the Presence of a Superplasticizer
,” ACI SP-119,
ACI
,
Detroit
,
1989
, pp.
171
-
188
.
7.
Mehta
,
P. K.
, “
Studies on Mechanisms by which Condensed Silica Fume Improves the Properties of Concrete
,”
Proceedings
,
CAN-MET workshop on condensed silica fume in concrete
,
Montreal, Canada
,
1987
.
8.
Aïtcin
,
P. C.
,
Sarkar
,
S. L.
, and
Diatta
,
Y.
, “
Microstructural Study of Different Types of Very High Strength Concretes
,”
Proceedings
,
Materials Research Society Symposium
, Vol.
85
,
1987
, pp.
261
-
272
.
Google Scholar
Crossref
Search ADS
 
9.
Ronneberg
,
H.
, and
Sandvik
,
M.
, “
High Strength Concrete for North Sea Platforms
,”
Concrete International
 0162-4075, Vol.
12
, No.
1
,
1990
, pp.
29
-
34
.
10.
High-Strength Concrete in Chicago High-Rise Buildings, Chicago Committee on High-Rise Buildings
, Report No. 5,
1977
.
11.
Cook
,
J. E.
, “
Research and Application of High-Strength Concrete Using Class C Fly Ash
,”
Concrete International
 0162-4075, Vol.
4
, No.
7
,
1982
, pp.
72
-
80
.
12.
Cook
,
J. E.
, “
10,000 psi Concrete
,”
Concrete International
 0162-4075, Vol.
11
, No.
10
,
1989
, pp.
67
-
75
.
13.
Ryell
,
J.
 and
Bickley
,
J. A.
, “
Scotia Plaza, High-Strength Concrete for Tall Buildings
,”
Proceedings
,
Conference on Utilization of High Strength Concrete
,
Stavanger, Norway
,
1987
, pp.
641
-
654
.
14.
Kawai
,
T.
,
Yamazaki
,
N.
,
Imai
,
M.
,
Tachibana
,
D.
, and
Inada
,
Y.
, “
Study on Application of 100 MPa Strength Concrete
,” personal communication,
Shimizu Corp.
,
Tokyo
, Japan, 1989.
15.
Read
,
P.
,
Carette
,
G.
, and
Malhotra
,
V. M.
, “
Strength Development Characteristics of High-Strength Concrete Incorporating Supplementary Cementing Materials
,”
Proceedings
,
Symposium on Utilization of High-Strength Concrete
,
Berkeley, CA
,
05
1990
.
16.
Aïtcin
,
P. C.
,
Laplante
,
P.
, and
Bedard
,
C.
, “
Development and Experimental Use of a 90 MPa Concrete
,” ACI SP-87,
ACI
,
Detroit
,
1985
, pp.
51
-
70
.
17.
Mehta
,
P. K.
, “
Durability of Concrete Exposed to Marine Environment
,” ACI SP-109,
ACI
,
Detroit
,
1988
, pp.
1
-
28
.
18.
Mass
,
G. R.
, “
Premixed Cement Paste
,”
Concrete International
 0162-4075, Vol.
11
, No.
11
,
1989
, pp.
82
-
85
.
19.
Asselanis
,
J.
,
Aïtcin
,
P. C.
, and
Mehta
,
P. K.
, “
Effect of Curing Conditions on the Compressive Strength and Elastic Modulus of Very High Strength Concrete
,”
Cement, Concrete, and Aggregates
, Vol.
10
, No.
1
,
1989
, pp.
80
-
83
.
This content is only available via PDF.
All rights reserved. This material may not be reproduced or copied, in whole or in part, in any printed, mechanical, electronic, film, or other distribution and storage media, without the written consent of ASTM International.
You do not currently have access to this content.