Journal Articles
Publisher: ASTM International
Article Type: Technical Papers
Matls. Perf. Charact.. August 2021, 10(1): 297–316.
Paper No: MPC20200049
Published Online: April 21, 2021
...Witor Wolf; Lóren Kelly de Paula Inácio; Dagoberto Brandão Santos The present work evaluates the precipitation of secondary phases in a cold-rolled ultrafine-grained 2205 duplex stainless steel after aging at temperatures ranging from 600°C to 950°C for different annealing times (300–86,400 s). X...
Journal Articles
Publisher: ASTM International
Article Type: Research-Article
Matls. Perf. Charact.. November 2017, 6(5): 807–822.
Paper No: MPC20170011
Published Online: September 12, 2017
... under certain situations, are finally addressed. Keywords aluminum, heat treatment, strengthening method, aging, casting alloys Introduction The use of aluminum alloys has recently increased in a wide number of applications, especially in the automotive field. This is not only due to the high strength...
Journal Articles
Publisher: ASTM International
Article Type: Research-Article
Matls. Perf. Charact.. October 2017, 6(4): 554–560.
Paper No: MPC20160094
Published Online: August 25, 2017
... to suitable heat treatment. In this work, the mechanical characteristics of conventional aging were compared with plasma nitrocarburizing in the Fe-31.2Mn-7.5Al-1.3Si-0.9C (wt. %) steel. The layers produced were characterized using optical micrograph and hardness and wear tests. The treatment produced layers...
Journal Articles
Publisher: ASTM International
Article Type: Research-Article
Matls. Perf. Charact.. August 2016, 5(5): 675–688.
Paper No: MPC20160034
Published Online: December 22, 2016
...I. A. Sustaita-Torres; S. Haro-Rodríguez; R. Colás The changes in microstructure that took place in two heat-resistant after aging alloys at 750°C for a period of time of up to 1000 h are reported in this work. The alloys selected had a similar composition, with the exception in carbon content...
Journal Articles
Publisher: ASTM International
Article Type: Research-Article
Matls. Perf. Charact.. July 2016, 5(1): 38–46.
Paper No: MPC20150039
Published Online: February 26, 2016
... in oil and the samples were subsequently aged at 500, 550, and 600°C. The solution annealed samples exhibited an average hardness of 30 Hardness Rockwell–Scale C and after the aging treatments, the hardness increased to 46 HRC. The hardness increases during the aging treatments were very fast. A 5 min...