Abstract
Films have been prepared with not only high hardness to guarantee excellent wear resistance but also high toughness to prevent brittle fracture at low to middle-high temperatures. On the basis of ternary transition metal nitrides with significantly improved hardness and toughness, TaMoN–Ag films with solute and nanocomposite structure were prepared by direct current (DC) magnetron sputtering technology. Friction wear tests were performed between room temperature (RT) and 700 °C. When doping with trace amounts of Ag atoms (∼1.12 at%, 4 W), TaMoN–Ag film maintain solid solution structure. TaMoN–Ag films with the Ag target power is 4 W show the highest hardness (H ∼ 62.1 GPa), which is 58% higher than TaMoN film and 44% better than that of TaMoN films. Meanwhile, a lower wear rate (KIC ∼ 5.87 × 10−7 mm3/N·m) is obtained. The tribological properties of TaMoN–Ag films at room temperatures are related to the H3/E2 and lubricious Ag phase, while the tribological properties at high temperatures are mainly due to the formation of lubricating binary metal oxides (AgxTMyOz (Magnéli phases)). The composite films generally have good resistance to plastic deformation.
References
1.
Ren
, P.
, Zhang
, K.
, He
, X.
, Du
, S.
, Yang
, X.
, An
, T.
, Wen
, M.
, and Zheng
, W.
, 2017
, “Toughness Enhancement and Tribochemistry of the Nb-Ag-N Films Actuated by Solute Ag
,” Acta Mater.
, 137
, pp. 1
–11
. 2.
Aouadi
, S. M.
, Singh
, D. P.
, Stone
, D. S.
, Polychronopoulou
, K.
, Nahif
, F.
, Rebholz
, C.
, Muratore
, C.
, and Voevodin
, A. A.
, 2010
, “Adaptive VN/Ag Nanocomposite Coatings With Lubricious Behavior From 25 to 1000 °C
,” Acta Mater.
, 58
(16
), pp. 5326
–5331
. 3.
Dai
, X.
, Wen
, M.
, Wang
, J.
, Cui
, X.
, Wang
, X.
, and Zhang
, K.
, 2020
, “The Tribological Performance at Elevated Temperatures of MoNbN-Ag Coatings
,” Appl. Surf. Sci.
, 509
, p. 145372
. 4.
Sliney
, H. E.
, Strom
, T. N.
, and Allen
, G. P.
, 1965
, “Fluoride Solid Lubricants for Extreme Temperatures and Corrosive Environments
,” ASLE Trans.
, 8
(4
), pp. 307
–322
. 5.
Harkonen
, E.
, Kolev
, I.
, Diaz
, B.
, Swiatowska
, J.
, Maurice
, V.
, Seyeux
, A.
, Marcus
, P.
, et al, 2014
, “Sealing of Hard CrN and DLC Coatings With Atomic Layer Deposition
,” ACS Appl. Mater. Interfaces
, 6
(3
), pp. 1893
–1901
. 6.
Sangiovanni
, D. G.
, 2018
, “Inherent Toughness and Fracture Mechanisms of Refractory Transition-Metal Nitrides via Density-Functional Molecular Dynamics
,” Acta Mater.
, 151
, pp. 11
–20
. 7.
Li
, H.
, Li
, J.
, Kong
, J.
, Huang
, J.
, Wu
, Q.
, and Xiong
, D.
, 2023
, “Achieving High Toughness and Wear Resistance for Hard TaN-Ag Films Actuated by Ag
,” Int. J. Refract. Met. Hard Mater.
, 111
, p. 106076
. 8.
Zhou
, Z.
, Rainforth
, W. M.
, Luo
, Q.
, Eh Hovsepian
, P.
, Ojeda
, J. J.
, and Romero-Gonzalez
, M. E.
, 2010
, “Wear and Friction of TiAlN/VN Coatings Against Al2O3 in Air at Room and Elevated Temperatures
,” Acta Mater.
, 58
(8
), pp. 2912
–2925
. 9.
Hu
, J.
, Li
, H.
, Li
, J.
, Wu
, Q
, Huang
, J.
, Kong
, J.
, Shi
, Y.
, et al, 2022
, “Effect of Ag Target Power on Structure, Mechanical Properties of TaC–Ag Films
,” Ceram. Int.
, 48
(8
), pp. 11718
–11728
. 10.
Chen
, Y.-I.
, Lin
, J.-H.
, and Chou
, C.-C.
, 2016
, “Oxidation Resistance and Mechanical Properties of Ta–Al–N Coatings
,” Surf. Coat. Technol.
, 303
, pp. 41
–47
. 11.
Li
, H.
, Li
, J.
, Kong
, J.
, Huang
, J.
, Wu
, Q.
, and Xiong
, D.
, 2023
, “Hard and Tough Sub-Stoichiometric B1 Ta-Mo-Nx Films by Regulating N Content
,” J. Alloys Compd.
, 934
, p. 168009
. 12.
Li
, H.
, Li
, J.
, Kong
, J.
, Huang
, J.
, Wu
, Q.
, and Xiong
, D.
, 2023
, “Structure and Mechanical Properties of Toughening B1 Ta1-XMoxN Films With Various Mo Contents
,” Ceram. Int.
, 49
(11
), pp. 18104
–18113
. 13.
Li
, Q.
, Ding
, C.
, Yang
, M.
, Yang
, M.
, Gao
, T.
, Zhang
, S.
, Ji
, B.
, Goto
, T.
, and Tu
, R.
, 2024
, “Corrosion Resistance and Conductivity of Ta-Nb-N-Coated 316L Stainless Steel as Bipolar Plates for Proton Exchange Membrane Fuel Cells
,” Coatings
, 14
(5
), p. 542
. 14.
Glechner
, T.
, Lang
, S.
, Hahn
, R.
, Alfreider
, M.
, Moraes
, V.
, Primetzhofer
, D.
, Ramm
, J.
, Kolozsvári
, S.
, Kiener
, D.
, and Riedl
, H.
, 2020
, “Correlation Between Fracture Characteristics and Valence Electron Concentration of Sputtered Hf-CN Based Thin Films
,” Surf. Coat. Technol.
, 399
, p. 126212
. 15.
Fang
, W.
, Yu
, H.
, Chang
, R.
, Zhang
, X.
, Ji
, P.
, Liu
, B.
, Li
, J.
, Qu
, X.
, Liu
, Y.
, and Yin
, F.
, 2019
, “Microstructure and Mechanical Properties of Cr-Rich Co-Cr-Fe-Ni High Entropy Alloys Designed by Valence Electron Concentration
,” Mater. Chem. Phys.
, 238
, p. 121897
. 16.
Zhou
, R.
, Ju
, H.
, Liu
, S.
, Zhao
, Z.
, Xu
, J.
, Yu
, L.
, Qian
, H.
, Jia
, S.
, Song
, R.
, and Shen
, J.
, 2022
, “The Influences of Ag Content on the Friction and Wear Properties of TiCN–Ag Films
,” Vacuum
, 196
, p. 110719
. 17.
Panda
, M.
, Krishnan
, R.
, Krishna
, N. G.
, Amirthapandian
, S.
, Magudapathy
, P.
, and Kamruddin
, M.
, 2019
, “Tuning the Tribological Property of PLD Deposited DLC-Au Nanocomposite Thin Films
,” Ceram. Int.
, 45
(7
), pp. 8847
–8855
. 18.
Cai
, Z.
, Chen
, R.
, Wang
, W.
, Qian
, J.
, Guo
, W.
, and Pu
, J.
, 2020
, “Microstructure and Tribological Properties of Cu-Doped VCN Films: The Role of Cu
,” Appl. Surf. Sci.
, 510
, p. 145509
. 19.
Wang
, W.
, Pu
, J.
, Cai
, Z.
, Zheng
, S.
, and Wei
, Y.
, 2020
, “Insights Into Friction Properties and Mechanism of Self-Lubricating MoVN–Ag Films at High Temperature
,” Vacuum
, 176
, p. 109332
. 20.
Bian
, S.
, Yu
, L.
, Xu
, J.
, and Xu
, J.
, 2022
, “Impact of Ag on the Microstructure and Tribological Behaviors of Adaptive ZrMoN–Ag Composite Lubricating Films
,” J. Mater. Res. Technol.
, 19
, pp. 2346
–2355
. 21.
Ju
, H.
, Yu
, D.
, Yu
, L.
, Ding
, N.
, Xu
, J.
, Zhang
, X.
, Zheng
, Y.
, Yang
, L.
, and He
, X.
, 2018
, “The Influence of Ag Contents on the Microstructure, Mechanical and Tribological Properties of ZrN-Ag Films
,” Vacuum
, 148
, pp. 54
–61
. 22.
Chen
, T.
, Yu
, L.-H.
, and Xu
, J.-H.
, 2018
, “Influence of Ag Content on the Microstructure, Mechanical, and Tribological Properties of TaVN–Ag Films
,” Int. J. Miner. Metall. Mater.
, 25
, pp. 110
–115
. 23.
Fenker
, M.
, Balzer
, M.
, Kellner
, S.
, Polcar
, T.
, Richter
, A.
, Schmidl
, F.
, and Vitu
, T.
, 2021
, “Formation of Solid Lubricants During High Temperature Tribology of Silver-Doped Molybdenum Nitride Coatings Deposited by dcMS and HIPIMS
,” Coatings
, 11
(11
), p. 1415
. 24.
Jin
, Y. S.
, Li
, M. Y.
, and Wang
, Y.
, 1994
, “The Synergistic Effects of Mo as an Alloy Element Added to Chromium Carbide Coatings on Their Lubrication Properties at High Temperatures
,” Wear
, 172
(2
), pp. 147
–154
. 25.
Liu
, Y.
, Li
, H.
, Li
, J.
, Zhao
, X.
, Huang
, J.
, Kong
, J.
, Wu
, Q.
, Shi
, Y.
, Zhang
, G.
, and Xiong
, D.
, 2023
, “Effect of W Content on Mechanical and Tribological Behaviors of Hard Ta1-XWxN Films
,” Int. J. Refract. Met. Hard Mater.
, 115
, p. 106271
. 26.
Fillot
, N.
, Iordanoff
, I.
, and Berthier
, Y.
, 2007
, “Wear Modeling and the Third Body Concept
,” Wear
, 262
(7–8
), pp. 949
–957
. 27.
Wei
, N.
, Li
, H.
, Li
, J.
, Sun
, L.
, Huang
, J.
, Kong
, J.
, Wu
, Q.
, Shi
, Y.
, and Xiong
, D.
, 2024
, “Structure, Mechanical, Tribological Properties and Corrosion Resistance of C/N Dual Doing Mo-SCN Films
,” Appl. Surf. Sci.
, 646
, p. 158905
. 28.
Chmielewski
, A.
, Nelayah
, J.
, Amara
, H.
, Creuze
, J.
, Alloyeau
, D.
, Wang
, G.
, and Ricolleau
, C.
, 2018
, “Direct Measurement of the Surface Energy of Bimetallic Nanoparticles: Evidence of Vegard’s Rulelike Dependence
,” Phys. Rev. Lett.
, 120
(2
), p. 025901
. 29.
Han
, L.
, Jeurgens
, L. P.
, Cancellieri
, C.
, Wang
, J.
, Xu
, Y.
, Huang
, Y.
, Liu
, Y.
, and Wang
, Z.
, 2020
, “Anomalous Texture Development Induced by Grain Yielding Anisotropy in Ni and Ni-Mo Alloys
,” Acta Mater.
, 200
, pp. 857
–868
. 30.
Seita
, M.
, Pecnik
, C. M.
, Frank
, S.
, and Spolenak
, R.
, 2010
, “Direct Evidence for Stress-Induced Texture Evolution and Grain Growth of Silver Thin Films Upon Thermal Treatment and Self-Ion Bombardment
,” Acta Mater.
, 58
(19
), pp. 6513
–6525
. 31.
Xiao
, J.
, Qi
, M.
, Gong
, C.
, Wang
, Z.
, Jiang
, A.
, Ma
, J.
, and Cheng
, Y.
, 2018
, “Crystal Structure and Optical Properties of Silver-Doped Copper Nitride Films (Cu3N:Ag) Prepared by Magnetron Sputtering
,” J. Phys. D: Appl. Phys.
, 51
(5
), p. 055305
. 32.
Ju
, H.
, Zhou
, R.
, Luan
, J.
, Yu
, L.
, Xu
, J.
, Zuo
, B.
, Yang
, J.
, Geng
, Y.
, Zhao
, L.
, and Fernandes
, F.
, 2022
, “Multilayer Mo2N-Ag/SiNx Films for Demanding Applications: Morphology, Structure and Temperature-Cycling Tribological Properties
,” Mater. Des.
, 223
, p. 111128
. 33.
Chun
, W.-J.
, Ishikawa
, A.
, Fujisawa
, H.
, Takata
, T.
, Kondo
, J. N.
, Hara
, M.
, Kawai
, M.
, Matsumoto
, Y.
, and Domen
, K.
, 2003
, “Conduction and Valence Band Positions of Ta2O5, TaON, and Ta3N5 by UPS and Electrochemical Methods
,” J. Phys. Chem. B
, 107
(8
), pp. 1798
–1803
. 34.
Jiang
, Y.
, Wu
, X.
, Bian
, S.
, Chen
, C.
, Han
, H.
, Zuo
, B.
, Lu
, K.
, Zhao
, L.
, Yu
, L.
, and Xu
, J.
, 2024
, “Insight Into the Tribological Performance and Mechanisms of MoN-Ag/Oil Solid-Liquid Lubrication System Based on Catalytic Effect
,” Surf. Coat. Technol.
, 480
, p. 130612
. 35.
Yuan
, Z.
, Li
, Y.
, Sun
, L.
, Yang
, J.
, Mei
, S.
, Xiong
, X.
, Fang
, Q.
, Chen
, Z.
, and Liu
, Y.
, 2024
, “Microstructures and Tribological Properties of MoS2/Mo2N Multilayer Gradient Films Deposited by Reactive Magnetron Sputtering
,” J. Mater. Res. Technol.
, 31
, pp. 1507
–1517
. 36.
Gao
, H.
, Li
, Y.
, Li
, C.
, Ma
, F.
, Song
, Z.
, and Xu
, K.
, 2016
, “Tuning the Electronic Properties in TaNx/Ag Nanocomposite Thin Films
,” RSC Adv.
, 6
(37
), pp. 30998
–31004
. 37.
Onoprienko
, A. A.
, and Ivashchenko
, V. I.
, 2021
, “Solid Solutions in Films of Ternary Carbides and Nitrides of Groups IV–VI Transition Metals: Structure and Properties
,” J. Superhard Mater.
, 43
, pp. 231
–247
. 38.
Brice
, D. K.
, Tsao
, J. Y.
, and Picraux
, S. T.
, 1989
, “Partitioning of Ion-Induced Surface and Bulk Displacements
,” Nucl. Instrum. Methods Phys. Res., Sect. B
, 44
(1
), pp. 68
–78
. 39.
Glechner
, T.
, Mayrhofer
, P. H.
, Holec
, D.
, Fritze
, S.
, Lewin
, E.
, Paneta
, V.
, Primetzhofer
, D.
, Kolozsvári
, S.
, and Riedl
, H.
, 2018
, “Tuning Structure and Mechanical Properties of Ta-C Coatings by N-Alloying and Vacancy Population
,” Sci. Rep.
, 8
(1
), p. 17669
. 40.
Chen
, X.
, Du
, Y.
, and Chung
, Y.-W.
, 2019
, “Commentary on Using H/E and H3/E2 as Proxies for Fracture Toughness of Hard Coatings
,” Thin Solid Films
, 688
, p. 137265
. 41.
Xu
, Y.
, Chen
, G.
, Liu
, Z.
, Zhu
, J.
, Shen
, J.
, Guo
, S.
, and Zhang
, X.
, 2023
, “Scratch Behaviors of Polyacrylate-Based Hard Coatings on Alternating Multi-Layered PMMA+ PC Substrates
,” Wear
, 530
, p. 204997
. 42.
Zhang
, S.
, 2015
, Thin Films and Coatings: Toughening and Toughness Characterization
, CRC Press
, Boca Raton, FL
.43.
Zhao
, D.
, Wang
, Y.
, Jiang
, X.
, Duan
, W.
, and Wang
, L.
, 2018
, “Microstructure Evolution, Wear and Corrosion Resistance of CrC Nanocomposite Coatings in Seawater
,” Appl. Surf. Sci.
, 457
, pp. 914
–924
. 44.
Zhang
, S.
, Sun
, D.
, Fu
, Y.
, and Du
, H.
, 2005
, “Toughness Measurement of Thin Films: A Critical Review
,” Surf. Coat. Technol.
, 198
(1–3
), pp. 74
–84
. 45.
Lawn
, B. R.
, Evans
, A. G.
, and Marshall
, D. B.
, 1980
, “Elastic/Plastic Indentation Damage in Ceramics: The Median/Radial Crack System
,” J. Am. Ceram. Soc.
, 63
(9–10
), pp. 574
–581
. 46.
Ortiz-Merino
, J. L.
, and Todd
, R. I.
, 2005
, “Relationship Between Wear Rate, Surface Pullout and Microstructure During Abrasive Wear of Alumina and Alumina/SiC Nanocomposites
,” Acta Mater.
, 53
(12
), pp. 3345
–3357
. 47.
Ping
, R.
, Zhang
, K.
, Wen
, M.
, Du
, S.
, Chen
, J.
, and Zheng
, W.
, 2018
, “The Roles of Ag Layers in Regulating Strengthening-Toughening Behavior and Tribochemistry of the Ag/TaC Nano-Multilayer Films
,” Appl. Surf. Sci.
, 445
, pp. 415
–423
. 