In the fabrication of carbon-carbon (C/C) composites, the first carbonization process is crucial, as the mechanical properties of the composite are completely altered at this stage. Some predominant effects of this process, in the composite, are development of delaminations, fiber breaks, distributed porosity and formation of transverse cracks in the matrix. These effects are to some extent, beneficial, during latter processing of the composite. However, excessive occurrence of any of these effects is undesirable. Keeping this in view, the present study focuses on the utilization of acoustic emission (AE) (as a nondestructive evaluation (NDE)) technique for identification and characterization of failure modes of C/C composites at several processing stages of C/C composites. Primarily, acoustic emission (AE) has been used to study the failure modes of C/C composites at the as-cured, carbonized and densified stages using AE parameters such as the peak amplitude, event duration and energy content of the AE signals. These parameters have been related to the initiation and progression of matrix cracking, fiber breakage and delaminations which occur in the composite at the as-cured, carbonized and densified stages.

Issue Section:
Research Papers
Topics:
Acoustic emissions, Carbon, Composite materials, Failure mechanisms, Delamination, Fibers, Nondestructive evaluation, Cracking (Materials), Fracture (Materials), Fracture (Process), Manufacturing, Mechanical properties, Porosity, Signals
1.
Gorman
M.
,
1991
, “
Acoustic Emission in 2D Carbon-Carbon Coupons in Tension
,”
Journal of Composite Materials
, Vol.
25
, June, pp.
703
–
714
.
2.
Tittmann, B. R., 1989, “Acoustical Studies of Damage Mechanisms in Carbon-Carbon during First Carbonization,” Proceedings of the IEEE Ultrasonics Symposium, pp. 627–630.
3.
Fitzer
E.
,
1990
, “
The Future of Carbon-Carbon Composites
,”
Carbon
, Vol.
25
, No.
2
, pp.
163
–
190
.
4.
Vaidya, U. K., 1993, “Nondestructive Evaluation of Graphite Fiber Based Composites using Acoustic and Vibration Techniques,” PhD Dissertation, Auburn University, Auburn, AL.
5.
Valentin
D.
,
1985
, “
A Critical Analysis of Amplitude Histograms Obtained During Acoustic Emissions Tests on Unidirectional Composites with an Epoxy and a PSP Matrix
,”
Composites
, Vol.
16
, No.
3
pp.
225
–
230
.
6.
Madhukar and Awerbuch, J., 1988, “Monitoring Damage Progression in Center Notched Boron Aluminum Laminates through Acoustic Emission,” ASTM STP 893, W. S. Johnson, ed., pp. 337–367.
7.
Fuwa
M.
,
Bunsell
A. R.
, and
Harris
B.
,
1975
, “
Tensile Failure Mechanisms in Carbon Fiber-Epoxy Composites
,”
Journal of Materials Science
, Vol.
10
, pp.
2062
–
2070
.
8.
Ghaffari, S., and Awerbuch, J., 1990, “On the Correlation between Acoustic Emission and Progression of Matrix Splitting in a Unidirectional Graphite/Epoxy Composite,” ASTM STP 1077, Acoustic Emission: Current Practice and Future Directions, Sachse, W., Roget, J., and Yamaguchi, K. eds., pp. 404–415.
9.
Berthelot
J. M.
, and
Rhazi
J.
,
1990
, “
Acoustic Emission in Carbon Fibre Composites
,”
Composites Science and Technology
, Vol.
37
, pp.
411
–
428
.
10.
Prewo
K.
,
1982
, “
A Compliant High Strain, Fibre-Reinforced Glass-Matrix Composite
,”
Journal of Materials Science
, Vol.
17
, pp.
3549
–
3563
.
11.
Vaidya, U. K., Raju, P. K., and Crocker, M. J., 1991, “Acoustic Emission Studies on Carbon-Carbon Composites,” NOISE-CON 91, D. A. Quinlan and M. G. Prasad, eds., pp. 165–169.
12.
Bhat, M. R., 1991, “A Study on Acoustic Emission Characterization of Fatigue Damage in Unidirectional Glass Fiber Composites,” M.S. Thesis, Indian Institute of Science, Bangalore, India.
13.
SAS Users Guide, SAS Institute, NC.
This content is only available via PDF.
Copyright © 1996
 by The American Society of Mechanical Engineers
You do not currently have access to this content.